EP076405(2)
It is a flame-retardant thermoplastic engineering material. The material fulfills flame retardancy according to UL 94 V-0 (@2.0mm), offering unique advantages in flame retardancy, water resistance, weatherability, UV resistance, and thermal stability. This material also boasts great impact strength and interlayer adhesion, making it ideal for applications such as automotive parts, industrial components, outdoor facilities and equipment, architectural decorative items, and large-scale sculptures.
Nozzle Temperature: 240-280℃
Build Plate Temp.: 80-100℃
Build Plate Material: Glass、PEI、Steel Spring Build Plate
Bottom Layer Printing Temp.: 250-260℃
Enclosed-chamber Printing: Yes
Print Speed: 60-200mm/s
Drying recommendations: 80°C in a hot air dryer for 4hours
Tensile Strength(X-Y): 42MPa
Tensile Modulus( X-Y): 2000MPa
Tensile Strength(Z): 20MPa
Tensile Modulus (Z): 1600MPa
Flexural Strength: 64MPa
Flexural Modulus: 2000MPa
Impact Strength, Notched: 18kJ/m2
Heat Deflection Temperature：99℃