EP112606BK001
It is a high-performance modified PPS material designed for FDM 3D printing technology. It features exceptional mechanical strength, high-temperature resistance, and resistance to weather, corrosion, and wear, as well as flame retardancy and electrical insulation, delivering outstanding overall performance. Printed parts exhibit low shrinkage and excellent dimensional stability, maintaining high strength retention even under high-temperature, high-humidity, and variable-frequency conditions. This material meets a flame retardancy rating of V0 (UL94, 0.8mm) and is suitable for applications in automotive, electronics, machinery, chemical engineering, sports equipment, and other industries.
Nozzle Temperature: 320-340°C
Build Plate Temp.: 100°C
Build Plate Material: PEI Build Plate
Bottom Layer Printing Temp.: 340°C
Enclosed-chamber Printing: Yes
Print Speed: 60-150mm/s
Drying recommendations: 80-100°C in a hot air dryer for 4-6hours
Tensile Strength(X-Y): 95MPa
Tensile Modulus( X-Y): 6500MPa
Tensile Strength(Z): 40MPa
Tensile Modulus (Z): 3000MPa
Flexural Strength: 155MPa
Flexural Modulus: 8300MPa
Impact Strength, Notched: 11kJ/m2
HDT: 208°C
Flame Retardancy: V0（UL94,0.8mm）